不管是什么材料制作的手板模型，當它超出了一定的使用條件限制，可能就會出現手板模型變形或是裂紋，那么遇到手板模型產生變形或是裂紋應該怎么做?還有沒有方法可以補救?下面濟南手板加工廠就來給大家說說手板模型產生變形或是裂紋的補救措施，大家可以看看內容了解一下。

No matter what kind of material is used for the prototype, when it exceeds certain service conditions, the prototype may be deformed or cracked. What should we do if the prototype is deformed or cracked? Is there any way to remedy it? Next, Jinan Handboard Processing Factory will talk about the remedial measures for the deformation or crack of the handboard model. You can have a look at the contents to understand.

1、手板發生變形后，其內部存在一定的殘余應力。在對手板加工前應該應力。可以使用應力退火和自然時效來使內部應力消失。

1. After the hand board is deformed, there is a certain residual stress in it. The stress shall be relieved before the fabrication of the handboard. Stress annealing and natural aging can be used to eliminate internal stress.

2、手板熱裂紋多數是由于機械應力造成，是在金屬凝固所造成的裂紋。解決辦法是改良手板結構，使其與金屬接觸的面更少。另外一種辦法是在控制金屬的含硫量而增加金屬的熱脆性。

2. Most of the hot cracks in the hand board are caused by mechanical stress, which is caused by metal solidification. The solution is to improve the structure of the hand board so that it has less contact with the metal. Another method is to increase the thermal brittleness of metals by controlling the sulfur content of metals.

3、手板冷裂紋是在低溫下所產品的裂紋。這是由于手板變形引致的，常常出現在手板受拉伸的地方，冷裂紋一般比較細小，但這種裂紋是不可逆的缺陷，只能重做。在制作大型而薄的手板時，常發生冷裂紋。相似，預防辦法也是減小內部應力和控制金屬中磷的含量。

3. The cold crack of the hand board is the crack of the product at low temperature. This is caused by the deformation of the hand board, which often occurs in the place where the hand board is stretched. The cold crack is generally small, but this crack is irreversible and can only be redone. Cold cracks often occur when making large and thin hand boards. Similarly, the preventive measures are to reduce the internal stress and control the phosphorus content in the metal.

可以看出一旦手板模型發生變形和裂紋，補救措施非常麻煩，甚有些變形和裂紋是無法補救的，是手板模型的重大缺陷，所以變形和裂紋是以預防措施為主，盡量避免出現變形和裂紋。更多相關內容就來我們網站http://m.csguangliang.com咨詢了解吧！

It can be seen that once the hand model is deformed and cracked, the remedial measures are very troublesome, and even some of the deformations and cracks can not be remedied, which are major defects of the hand model. Therefore, the deformation and cracks are mainly preventive measures to avoid deformation and cracks as much as possible. More relevant content will come to our website http://m.csguangliang.com Ask and understand!